LATI Latiohm 66-04 PD01 G/25-V0CT1 PA66, 25% Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | LATI |
| Trade Name | Latiohm |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latiohm 66-04 PD01 G/25-V0CT1 PA66, 25% Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Semiconductive/dissipative product based on Polyamide 66 (PA66). Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0055 cm/cm | 0.0030 - 0.0055 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0065 - 0.0095 cm/cm | 0.0065 - 0.0095 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | |
| Elongation at Break | 2.4 % | 2.4 % | |
| Tensile Modulus | 17.0 GPa | 2470 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | |
| Vicat Softening Point | 215 °C @Load 5.00 kg |
419 °F @Load 11.0 lb |
|
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
||
| Oxygen Index | 36 % | 36 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2500 ohm | 2500 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS (Europe-Africa-Middle East)
- Lucas-Milhaupt Silvaloy® A24 Brazing Alloy
- Chase Plastics CP Pryme® NN100STL (COND, 50% RH) Nylon 66, Super Toughened, Internally Lubricated
- Universal Wire Works 99 Nickel Alloy Welding Wire
- A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
- BNZ Materials No. 2986 Mortar
- 3M Scotch-Weld™ LO100 Low Odor Instant Adhesive
- Aclo Accuguard Polypropylene CP0467V0CSV Copolymer Flame Retardant Automotive Approved grade
- Quadrant EPP Quadrant Nylon 105 Black
- LATI Latilub 88/10-15T G/30 PEEK, 30% Glass Fiber Reinforced, PTFE Filled
Copyright © lookpolymers.com All Rights Reserved