LATI Latiohm 66-06 PD03 G/20 PA66, 20% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer LATI
Trade Name Latiohm
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latiohm 66-06 PD03 G/20 PA66, 20% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semiconductive/dissipative product based on Polyamide 66 (PA66). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0055 cm/cm
0.0040 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0090 - 0.012 cm/cm
0.0090 - 0.012 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa

@Temperature 120 °C
 13100 psi

@Temperature 248 °F
120 MPa

@Temperature 90.0 °C
 17400 psi

@Temperature 194 °F
135 MPa

@Temperature 60.0 °C
 19600 psi

@Temperature 140 °F
180 MPa

@Temperature 23.0 °C
 26100 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
3.6 %

@Temperature 60.0 °C
 3.6 %

@Temperature 140 °F
5.1 %

@Temperature 90.0 °C
 5.1 %

@Temperature 194 °F
5.9 %

@Temperature 120 °C
 5.9 %

@Temperature 248 °F
Tensile Modulus 5.80 GPa

@Temperature 120 °C
 841 ksi

@Temperature 248 °F
7.50 GPa

@Temperature 90.0 °C
 1090 ksi

@Temperature 194 °F
9.10 GPa

@Temperature 60.0 °C
 1320 ksi

@Temperature 140 °F
12.0 GPa

@Temperature 23.0 °C
 1740 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Surface Resistance 130000 ohm
130000 ohm
Processing Properties Metric English Comments
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa