LATI Latiohm 87/26-06 PD01-V1 PC, Flame Retardant

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer LATI
Trade Name Latiohm
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latiohm 87/26-06 PD01-V1 PC, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semiconductive/dissipative product based on Polycarbonate (PC). UL94 V-1 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0050 cm/cm
0.0025 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0075 cm/cm
0.0050 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
Elongation at Break 2.3 %
2.3 %
Tensile Modulus 7.80 GPa
1130 ksi
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.650 J/cm²
3.09 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Vicat Softening Point 145 °C

@Load 5.00 kg
293 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Oxygen Index 30 %
30 %
Glow Wire Test 925 °C

@Thickness 1.00 mm
1700 °F

@Thickness 0.0394 in
GWIT
925 °C

@Thickness 2.00 mm
1700 °F

@Thickness 0.0787 in
GWIT
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
GWFI/GWT
960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
GWFI/GWT
Electrical Properties Metric English Comments
Surface Resistance 5000 ohm
5000 ohm
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 100 - 120 °C
212 - 248 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa