LATI Latistat 52/7-02 MI/30 PP Homopolymer, 30% Mica Filled

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler
Manufacturer	LATI
Trade Name	Latistat
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latistat 52/7-02 MI/30 PP Homopolymer, 30% Mica Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Dissipative product based on Polypropylene homopolymer (PPh). Mica filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.22 g/cc	0.0441 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0080 - 0.010 cm/cm	0.0080 - 0.010 in/in
Linear Mold Shrinkage, Transverse	0.0085 - 0.0105 cm/cm	0.0085 - 0.0105 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	30.0 MPa	4350 psi
Elongation at Break	3.0 %	3.0 %
Elongation at Yield	1.5 %	1.5 %
Tensile Modulus	5.20 GPa	754 ksi
Charpy Impact Unnotched	1.00 J/cmÂ²	4.76 ft-lb/inÂ²
Charpy Impact, Notched	0.100 J/cmÂ²	0.476 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	140 Â°C	284 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	95.0 Â°C	203 Â°F
Vicat Softening Point	110 Â°C @Load 5.00 kg	230 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	800 ohm	800 ohm

Processing Properties	Metric	English
Melt Temperature	200 - 240 Â°C	392 - 464 Â°F
Mold Temperature	40.0 - 60.0 Â°C	104 - 140 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa

Users viewing this material also viewed the following: