LG Chemical 401 AF Flame Retardant HIPS

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical 401 AF Flame Retardant HIPS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NON-DECA, Flame retardant, Safety standards: listed with UL CSA, and classified according to IEC 707, Meet requirements for flammability, mechanical and electrical properties, uses non-bromide as flame retardant agent and has well-balanced mechanical properties, Applications include televisions, VTR, monitors, computers and other electrical electronic parts requiring flame retard
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
ASTM D955
Melt Flow 12 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 90
90
ASTM D785
Tensile Strength, Yield 24.6 MPa
3570 psi
50 mm/min; ASTM D638
Elongation at Break 50 %
50 %
50 mm/min; ASTM D638
Flexural Yield Strength 44.2 MPa
6410 psi
15 mm/min; ASTM D790
Flexural Modulus 2.20 GPa
319 ksi
15 mm/min; ASTM D790
Izod Impact, Notched 0.640 J/cm

@Thickness 6.35 mm
 1.20 ft-lb/in

@Thickness 0.250 in
 ASTM D256
0.880 J/cm

@Thickness 3.17 mm
 1.65 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C

@Thickness 12.7 mm
 167 °F

@Thickness 0.500 in
 Unannealed; ASTM D648
Vicat Softening Point 93.0 °C
199 °F
1000 g; ASTM D1525
Flammability, UL94 V-0
V-0
1/8 in
V-0
V-0
1/16 in
Electrical Properties Metric English Comments
Arc Resistance <= 60 sec
<= 60 sec
UL Rating PLC 7 (<60 sec)
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL Rating PLC 1 (400-600 volts)
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL Rating PLC 3 (15-30 sec)
High Amp Arc Ignition, HAI 60 - 120 arcs
60 - 120 arcs
UL Rating PLC 1 (60-120 arcs)
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
UL Rating PLC 1 (10-25.4 mm/min)
Descriptive Properties Value Comments
IEC 707 Flammability FVO mm/min.
1/16 in