LG Chemical ER460 ABS, Medium Heat Resistance, High Flowability

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical ER460 ABS, Medium Heat Resistance, High Flowability.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, Medium Heat Resistance, High FlowabilityApplication: Automobile, Motor Cycle, Electric & Electronic GoodsCAS No. 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0070 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 23 g/10 min

@Load 10.0 kg,
Temperature 220 °C
23 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength, Yield 48.1 MPa

@Thickness 3.20 mm
6970 psi

@Thickness 0.126 in
50 mm/min; ASTM D638
Elongation at Break 50 %

@Thickness 3.20 mm
50 %

@Thickness 0.126 in
50 mm/min; ASTM D638
Tensile Modulus 2.16 GPa

@Thickness 3.20 mm
313 ksi

@Thickness 0.126 in
1 mm/min; ASTM D638
Flexural Yield Strength 78.5 MPa

@Thickness 3.20 mm
11400 psi

@Thickness 0.126 in
15 mm/min; ASTM D790
Flexural Modulus 2.55 GPa

@Thickness 3.20 mm
370 ksi

@Thickness 0.126 in
15 mm/min; ASTM D790
Izod Impact, Notched 2.45 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
4.59 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
ASTM D256
2.45 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
4.59 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched 1.08 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
2.02 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
ASTM D256
1.18 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
2.20 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C

@Thickness 6.40 mm
205 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 91.0 °C

@Thickness 6.40 mm
196 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Vicat Softening Point 97.0 °C

@Load 5.00 kg
207 °F

@Load 11.0 lb
50°C/h; ASTM D1525
Processing Properties Metric English Comments
Rear Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Front Barrel Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Nozzle Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Melt Temperature 210 - 240 °C
410 - 464 °F
Injection Molding
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding