LG Chemical LUCON CP6080LP PC+CNT+GF
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON CP6080LP PC+CNT+GF.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC+CNT+GF, Electrostatic Dissipation, Low Surface TribochargeApplication: ATM parts, HDD BracketCAS No. 103598-77-2, 65997-17-3 and 7782-42-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 300 °C |
21 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 93.2 MPa @Thickness 3.20 mm |
13500 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 6.0 % @Thickness 3.20 mm |
>= 6.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 137 MPa @Thickness 3.20 mm |
19900 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Flexural Modulus | 4.90 GPa @Thickness 3.20 mm |
711 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C @Thickness 6.40 mm |
277 °F @Thickness 0.252 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+7 - 1.00e+11 ohm | 1.00e+7 - 1.00e+11 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Middle Barrel Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Front Barrel Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 5.00 - 7.00 hour | 5.00 - 7.00 hour | Injection Molding |
| Back Pressure | 0.000 - 1.96 MPa | 0.000 - 284 psi | Injection Molding |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nylene® 404 Nylon 6, 50% RH
- Quantum Composites QC-8100 60% Glass Fiber Vinyl Ester SMC (discontinued **)
- Wico Plast Wicotal 500 Acetal
- Ensinger Tecapeek® XP-117 Compression Molded PEEK Compound, 25% PTFE Filled
- Arkema Group Rilsan® MB 3750 Nylon 11, Transparent Grade (Dry)
- AK Steel ASTM A 570, Grade 30 Hot Rolled Carbon Steel, Structural Quality (SQ)
- BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Dry)
- Arkema Group Rilsan® BMN P40 D Nylon 11 (Conditioned)
- Arlon 55108R030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Plastcom SLOVASTER® B GF 20 FRL 4 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Bromine Hydrocarbon Flame Retardant
Copyright © lookpolymers.com All Rights Reserved