LG Chemical LUMID GP2130A(W) PA6+GF13%, General Purpose
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID GP2130A(W) PA6+GF13%, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6+GF13%, General PurposeApplication: Automotive PartsCAS No. 25038-54-4 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.012 cm/cm @Thickness 3.20 mm |
0.0070 - 0.012 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 5.0 % @Thickness 3.20 mm |
5.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 167 MPa @Thickness 3.20 mm |
24200 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 4.71 GPa @Thickness 3.20 mm |
683 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| UL RTI, Electrical | 65.0 °C @Thickness >=0.750 mm |
149 °F @Thickness >=0.0295 in |
|
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness >=0.750 mm |
149 °F @Thickness >=0.0295 in |
|
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness >=0.750 mm |
149 °F @Thickness >=0.0295 in |
|
| Flammability, UL94 | HB @Thickness >=0.750 mm |
HB @Thickness >=0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 1.00 mm |
508 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 160 sec | 160 sec | ASTM D495 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | |
| Hot Wire Ignition, HWI | 15 - 30 sec @Thickness >=0.750 mm |
15 - 30 sec @Thickness >=0.0295 in |
|
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 0.750 mm |
>= 120 arcs @Thickness 0.0295 in |
|
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 50.0 mm/min | 1.00 - 1.97 in/min |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 255 °C | 455 - 491 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Front Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Nozzle Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |