LG Chemical LUMID GP2259AFL PA6+GF25%, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name LUMID
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMID GP2259AFL PA6+GF25%, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PA6+GF25%, Flame RetardantApplication: IT/OA (Connector)CAS No. 25038-54-4, 65997-17-3, 1163-19-5, 1309-64-4 and 138265-88-0Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.60 g/cc
1.60 g/cc
ASTM D792
Water Absorption 0.70 %

@Temperature 23.0 °C,
Time 86400 sec
 0.70 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0090 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0090 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Yield 127 MPa

@Thickness 3.20 mm
 18500 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 3.0 %

@Thickness 3.20 mm
 3.0 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 186 MPa

@Thickness 3.20 mm
 27000 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 8.53 GPa

@Thickness 3.20 mm
 1240 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.981 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.84 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 41.0 µm/m-°C
22.8 µin/in-°F
ASTM D696
Melting Point 220 °C
428 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 205 °C

@Thickness 6.40 mm
 401 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 90.0 °C

@Thickness >=0.800 mm
 194 °F

@Thickness >=0.0315 in
90.0 °C

@Thickness >=3.00 mm
 194 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 90.0 °C

@Thickness >=0.800 mm
 194 °F

@Thickness >=0.0315 in
90.0 °C

@Thickness >=3.00 mm
 194 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 90.0 °C

@Thickness >=0.800 mm
 194 °F

@Thickness >=0.0315 in
90.0 °C

@Thickness >=3.00 mm
 194 °F

@Thickness >=0.118 in
Flammability, UL94 V-2

@Thickness >=0.800 mm
 V-2

@Thickness >=0.0315 in
V-2

@Thickness >=3.00 mm
 V-2

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 ASTM D150
Dielectric Strength 21.0 kV/mm

@Thickness 1.00 mm
 533 kV/in

@Thickness 0.0394 in
 ASTM D149
Arc Resistance 90 sec
90 sec
ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 270 °C
482 - 518 °F
Injection Molding
Middle Barrel Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Front Barrel Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Nozzle Temperature 260 - 285 °C
500 - 545 °F
Injection Molding
Melt Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding