LG Chemical LUPOL HF5157 PP+Rubber+MF, High Flow and Stiffness, High Impact
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced, Impact Modified |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL HF5157 PP+Rubber+MF, High Flow and Stiffness, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PP+Rubber+MF, High Flow and Stiffness, High Impact, Good Weatherability, Scratch ResistanceApplication: Automotive Exterior (Slim wall Bumper Fascia)Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.010 cm/cm @Thickness 3.20 mm |
0.0090 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.6 MPa @Thickness 3.20 mm |
2990 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 120 % @Thickness 3.20 mm |
120 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 15.7 MPa @Thickness 6.40 mm |
2280 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 1.86 GPa @Thickness 6.40 mm |
270 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.608 J/cm @Thickness 6.40 mm, Temperature -10.0 °C |
>= 1.14 ft-lb/in @Thickness 0.252 in, Temperature 14.0 °F |
ASTM D256 |
| >= 4.71 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
>= 8.82 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 87 General Purpose Acrylic Resin
- Polymax® Maxelast® A9960 TPE, ABS/PC Overmold
- PolyOne Dynaflex™ G2701-1000-02 Thermoplastic Elastomer (TPE)
- Solvay Chemicals SOLKANE® 407A
- Sharadaa Ceramics ZAP 008 Smart Cast Application
- Techmer ES Statiblend® HIPS E AS
- Teknor Apex APEX® 3301-75 Polyvinyl Chloride, Flexible
- Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled
- Atom Adhesives AA-DUCT 916 Epoxy Adhesive
- BASF Ultramid® B3WG5 BK 00564 25% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved