LG Chemical Lupox® LW5300M PBT+PC+MF30%

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer LG Chemical
Trade Name Lupox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupox® LW5300M PBT+PC+MF30%.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PBT+PC+MF30%, Low WarpageApplication: Automotive (Head Lamp Bezel)CAS No. 24968-12-5, 103598-77-2, 25038-59-9 and 14807-96-6Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0070 - 0.0090 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 57.9 MPa

@Thickness 3.20 mm
8400 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break 3.0 %

@Thickness 3.20 mm
3.0 %

@Thickness 0.126 in
5mm/min; ASTM D638
Flexural Yield Strength 97.1 MPa

@Thickness 3.20 mm
14100 psi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Flexural Modulus 5.30 GPa

@Thickness 3.20 mm
768 ksi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Izod Impact, Notched 0.392 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
0.735 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
@ Break; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 165 °C

@Thickness 6.40 mm
329 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 115 °C

@Thickness 6.40 mm
239 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 250 °C
455 - 482 °F
Injection Molding
Middle Barrel Temperature 240 - 250 °C
464 - 482 °F
Injection Molding
Front Barrel Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Nozzle Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Melt Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Injection Molding
Drying Temperature 120 °C
248 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding