LG Chemical MP211 ABS, Low Gloss, Metal Plating

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical MP211 ABS, Low Gloss, Metal Plating.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, High Flow, Metal PlatingApplication: Decorative Parts (Home Appliance Door Handle Etc)CAS No. 9003-56-9 and 9003-54-7Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 27 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 27 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Tensile Strength, Yield 43.1 MPa

@Thickness 3.20 mm
 6260 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 40 %

@Thickness 3.20 mm
 40 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 70.6 MPa

@Thickness 3.20 mm
 10200 psi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 2.35 GPa

@Thickness 3.20 mm
 341 ksi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 3.04 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 5.69 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
3.43 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 6.43 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 1.47 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 2.76 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
1.57 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 2.94 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 6.40 mm
 203 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C

@Thickness 6.40 mm
 189 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 95.0 °C

@Load 5.00 kg
 203 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
Flammability, UL94 HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Dielectric Strength 28.0 kV/mm
711 kV/in
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=1.50 mm
 15 - 30 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=3.00 mm
 15 - 30 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 25.4 - 50.0 mm/min
1.00 - 1.97 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Middle Barrel Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Front Barrel Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Nozzle Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Melt Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 68.6 - 88.3 MPa
9950 - 12800 psi
Injection Molding
Screw Speed <= 80 rpm
<= 80 rpm
Injection Molding