- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyethylene (PE)
- HDPE
- LG Chemical SEETEC PH162 HDPE
LG Chemical SEETEC PH162 HDPE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | LG Chemical |
| Trade Name | SEETEC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SEETEC PH162 HDPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Characteristics : Good balance of toughness & stiffness stressAdditives : Anti-Oxidants, LubricantsProcessing recommendations : Maintain the stock temperature 200-230°C (392-446°C) for optimum part qualityApplication: Utilized electrical conduit, corrugated pipeCAS No. 25213-02-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.955 - 0.958 g/cc | 0.955 - 0.958 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 200 hour | >= 200 hour | F50; ASTM D1693 |
| Melt Flow | 0.12 - 0.18 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.12 - 0.18 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 55 | 55 | ASTM D785 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 50mm/min; ASTM D638 |
| Tensile Strength, Yield | 26.5 MPa | 3840 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | >= 800 % @Thickness 50.0 mm |
>= 800 % @Thickness 1.97 in |
ASTM D638 |
| Flexural Modulus | 1.27 GPa | 185 ksi | ASTM D790 |
| Izod Impact, Notched | >= 1.96 J/cm @Temperature 23.0 °C |
>= 3.67 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 132 °C | 270 °F | 10°C/min; ASTM D3418 |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
Users viewing this material also viewed the following: