LG Chemical SH610A ABS, High Impact
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SH610A ABS, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Extrusion Molding, General Purpose, High ImpactApplication: Bag, Automobile InteriorCAS No. 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Extrusion Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 1.0 g/10 min @Load 3.50 kg, Temperature 230 °C |
1.0 g/10 min @Load 7.72 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Yield | 42.2 MPa @Thickness 3.20 mm |
6120 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 35 % @Thickness 3.20 mm |
35 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Yield | >= 5.0 % @Thickness 3.20 mm |
>= 5.0 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 63.7 MPa @Thickness 3.20 mm |
9250 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 4.22 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
7.90 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 4.90 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
9.18 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 94.0 °C @Load 5.00 kg |
201 °F @Load 11.0 lb |
50°C/h; ASTM D1525 |
| UL RTI, Electrical | 60.0 °C @Thickness >=1.50 mm |
140 °F @Thickness >=0.0591 in |
UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness >=1.50 mm |
140 °F @Thickness >=0.0591 in |
UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness >=1.50 mm |
140 °F @Thickness >=0.0591 in |
UL 746B |
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 210 °C | 356 - 410 °F | Extrusion Molding |
| Zone 2 | 190 - 230 °C | 374 - 446 °F | Extrusion Molding |
| Zone 3 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Zone 4 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Adapter Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Die Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Roll Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Bottom, Extrusion |
| 70.0 - 90.0 °C | 158 - 194 °F | Middle, Extrusion | |
| 70.0 - 100 °C | 158 - 212 °F | Top, Extrusion | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Extrusion Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |