LNP NORYL® EXCP0111 PPS + Polyphenylene Ether, 42% Glass / Mineral Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP NORYL® EXCP0111 PPS + Polyphenylene Ether, 42% Glass / Mineral Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
For applications requiring voltage resistance.Features: Corona resistantForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 101 MPa
14600 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 101 MPa
14600 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 1.5 %
1.5 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 1.5 %
1.5 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 11.3 GPa
1640 ksi
5 mm/min; ASTM D638
Flexural Strength 145 MPa
21000 psi
50.8 mm Span, 1 mm/min; ASTM D790
Flexural Modulus 10.2 GPa
1480 ksi
(50.8 mm Span) 1mm/min; ASTM D790
Izod Impact, Notched 0.374 J/cm
0.701 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.24 J/cm
4.20 ft-lb/in
ASTM D256
Falling Dart Impact 3.73 J
2.75 ft-lb
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 268 °C

@Thickness 3.18 mm
514 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 211 °C

@Thickness 3.18 mm
412 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 288 - 304 °C
550 - 579 °F
Middle Barrel Temperature 304 - 316 °C
579 - 601 °F
Front Barrel Temperature 316 - 332 °C
601 - 630 °F
Nozzle Temperature 304 - 321 °C
579 - 610 °F
Melt Temperature 304 - 332 °C
579 - 630 °F
Mold Temperature 138 - 160 °C
280 - 320 °F
Drying Temperature 141 °C
286 °F
Dry Time 3 - 4 hour
3 - 4 hour
Moisture Content 0.040 %
0.040 %
Suggested
Back Pressure 0.345 MPa
50.0 psi