LNP Stat-Kon® LC-1003 Polyetheretherketone, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Stat-Kon® LC-1003 Polyetheretherketone, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 191 MPa
27700 psi
ASTM D638
Tensile Strength, Yield 191 MPa
27700 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Elongation at Yield 2.0 %
2.0 %
ASTM D638
Tensile Modulus 16.8 GPa
2440 ksi
ASTM D638
Flexural Strength 296 MPa
42900 psi
ASTM D790
Flexural Modulus 13.0 GPa
1890 ksi
ASTM D790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.18 mm
1.20 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 6.41 J/cm

@Thickness 3.18 mm
12.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 7.50 kJ/m²
3.57 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
ISO 180
Falling Dart Impact 5.00 J
3.69 ft-lb
ASTM D3763
Impact Test 2.30 J
1.70 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 258 °C
496 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D4496
Processing Properties Metric English Comments
Melt Temperature 379 - 388 °C
714 - 730 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.010 %
0.010 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi