LNP Thermocomp® JF-1004 EM M BK905 Polyethersulfone, Milled Glass Fiber  (discontinued **)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® JF-1004 EM M BK905 Polyethersulfone, Milled Glass Fiber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.59 g/cc
1.59 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0070 cm/cm
0.0070 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 83.4 MPa
12100 psi
ASTM D638
Elongation at Break 3.6 %
3.6 %
ASTM D638
Flexural Strength 117 MPa
17000 psi
ASTM D790
Flexural Modulus 4.65 GPa
674 ksi
ASTM D790
Izod Impact, Notched 0.374 J/cm

@Thickness 3.18 mm
0.701 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.80 J/cm

@Thickness 3.18 mm
8.99 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 203 °C
397 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 354 - 371 °C
669 - 700 °F
Mold Temperature 135 - 149 °C
275 - 300 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.050 %
0.050 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi
Descriptive Properties Value Comments
Color Black