LNP Thermocomp® JF-1008 Polyethersulfone, Glass Fiber Reinforcement (discontinued **)

Category	Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LNP Thermocomp® JF-1008 Polyethersulfone, Glass Fiber Reinforcement (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

Physical Properties	Metric	English	Comments
Specific Gravity	1.66 g/cc	1.66 g/cc	Method A; ASTM D792

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	150 MPa	21800 psi	ASTM D638
Elongation at Break	2.1 %	2.1 %	ASTM D638
Izod Impact, Notched	0.961 J/cm @Thickness 3.18 mm	1.80 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	6.19 J/cm @Thickness 3.18 mm	11.6 ft-lb/in @Thickness 0.125 in	ASTM D256

Processing Properties	Metric	English	Comments
Melt Temperature	354 - 371 °C	669 - 700 °F
Mold Temperature	135 - 149 °C	275 - 300 °F
Drying Temperature	121 - 149 °C	250 - 300 °F
Dry Time	4 hour	4 hour
Moisture Content	0.050 %	0.050 %	Suggested
Back Pressure	0.345 - 0.689 MPa	50.0 - 99.9 psi