LNP Thermocomp® UF-1006 FR HS LEX BK8-115 Polyphthalamide, Glass Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® UF-1006 FR HS LEX BK8-115 Polyphthalamide, Glass Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Heat Stabilized, Flame RetardantForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.65 g/cc
1.65 g/cc
Method A; ASTM D792
Water Absorption 0.20 %
0.20 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 181 MPa
26300 psi
ASTM D638
Tensile Strength, Yield 181 MPa
26300 psi
ASTM D638
Elongation at Break 1.9 %
1.9 %
ASTM D638
Elongation at Yield 1.9 %
1.9 %
ASTM D638
Tensile Modulus 13.8 GPa
2000 ksi
ASTM D638
Flexural Strength 255 MPa
37000 psi
ASTM D790
Flexural Modulus 12.1 GPa
1750 ksi
ASTM D790
Izod Impact, Notched 0.907 J/cm

@Thickness 3.18 mm
1.70 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 5.50 J/cm

@Thickness 3.18 mm
10.3 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 44.7 kJ/m²
21.3 ft-lb/in²
ISO 180
Falling Dart Impact 2.90 J
2.14 ft-lb
ASTM D3763
Processing Properties Metric English Comments
Melt Temperature 299 - 310 °C
570 - 590 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi