LNP ULTEM® SMU5836 Polyetherimide, 30% Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP ULTEM® SMU5836 Polyetherimide, 30% Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High modulus with shielding/ conductive characteristics for high-heat applications.Features: Electrically Conductive, High Heat Resistance, High StrengthForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 172 MPa
24900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 4.4 %
4.4 %
Type I, 5 mm/min; ASTM D638
Flexural Strength 234 MPa
33900 psi
102 mm Span, 3 mm/min; ASTM D790
Flexural Modulus 15.1 GPa
2190 ksi
(102 mm Span) 3mm/min; ASTM D790
Izod Impact, Notched 0.427 J/cm
0.800 ft-lb/in
ASTM D256
Falling Dart Impact 6.89 J
5.08 ft-lb
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 6.35 mm
410 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 20 ohm-cm
20 ohm-cm
ASTM D257
Surface Resistance 3000 ohm
3000 ohm
ASTM D257
Static Decay <= 0.010 sec
<= 0.010 sec
5000V to <50V; FTMS101B
Processing Properties Metric English Comments
Rear Barrel Temperature 360 - 421 °C
680 - 790 °F
Middle Barrel Temperature 371 - 421 °C
700 - 790 °F
Front Barrel Temperature 382 - 427 °C
720 - 801 °F
Nozzle Temperature 377 - 421 °C
711 - 790 °F
Melt Temperature 382 - 427 °C
720 - 801 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 149 °C
300 °F
Dry Time <= 24 hour
<= 24 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi
Clamp Pressure 41.0 - 69.0 MPa
5950 - 10000 psi
Shot Size 40 - 60 %
40 - 60 %
Suggested
Vent Depth 0.00250 - 0.00760 cm
0.000984 - 0.00299 in
Screw Speed 40 - 70 rpm
40 - 70 rpm