Lanxess Durethan® AC 30 000000 Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AC 30 000000 Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, injection molding-grade, non-reinforced, higher notched impact strength than A 30 / A 31 in the dry and conditioned stateApplication Examples: plug connectors, cable binders, cable clips, parts with living hinges, furniture hinges
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Water Absorption 8.0 %
8.0 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 2.5 %
2.5 %
23°C/50% R.H.; Test Sim. to ISO 62
Mechanical Properties Metric English Comments
Tensile Strength, Yield 48.0 MPa
6960 psi
Conditioned; ISO 527-1/-2
80.0 MPa
11600 psi
ISO 527-1/-2
Elongation at Break 14 %
14 %
Nominal; ISO 527-1/-2
>= 50 %
>= 50 %
Nominal, Conditioned; ISO 527-1/-2
Elongation at Yield 5.0 %
5.0 %
ISO 527-1/-2
21 %
21 %
Conditioned; ISO 527-1/-2
Tensile Modulus 1.20 GPa
174 ksi
Conditioned; ISO 527-1/-2
2.90 GPa
421 ksi
ISO 527-1/-2
Charpy Impact Unnotched 20.0 J/cm²

@Temperature -30.0 °C
95.2 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Conditioned; ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eA
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eA
Impact 4314
4314
Puncture maximum force, Conditioned (N); ISO 6603-2
5050
5050
Puncture maximum force (N); ISO 6603-2
5977

@Temperature -30.0 °C
5977

@Temperature -22.0 °F
Puncture maximum force (N); ISO 6603-2
Puncture Energy 26.0 J
19.2 ft-lb
Conditioned; ISO 6603-2
32.0 J
23.6 ft-lb
ISO 6603-2
33.0 J

@Temperature -30.0 °C
24.3 ft-lb

@Temperature -22.0 °F
ISO 6603-2
33.0 J

@Temperature -30.0 °C
24.3 ft-lb

@Temperature -22.0 °F
Conditioned; ISO 6603-2
Tensile Creep Modulus, 1 hour 1100 MPa
160000 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 800 MPa
116000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
Melting Point 260 °C
500 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 53.0 °C
127 °F
ISO 75-1/-2
Vicat Softening Point 200 °C
392 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
IEC 60695-11-10
Oxygen Index 21 %
21 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
Conditioned; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
IEC 60250
3.6

@Frequency 100 Hz
3.6

@Frequency 100 Hz
IEC 60250
3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
Conditioned; IEC 60250
7.0

@Frequency 100 Hz
7.0

@Frequency 100 Hz
Conditioned; IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243-1
30.0 kV/mm
762 kV/in
Conditioned; IEC 60243-1
Dissipation Factor 0.0090

@Frequency 100 Hz
0.0090

@Frequency 100 Hz
IEC 60250
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
0.070

@Frequency 1.00e+6 Hz
0.070

@Frequency 1.00e+6 Hz
Conditioned; IEC 60250
0.14

@Frequency 100 Hz
0.14

@Frequency 100 Hz
Conditioned; IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Features High impact or high impact modified
Form Pellets
ISO Shortname ISO 1874-PA 66-I, MR, -030
Processing Injection molding