Lanxess Durethan® AKV 15 FN 00 000000 Nylon 66, 12% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AKV 15 FN 00 000000 Nylon 66, 12% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, 12% glass fiber, injection molding, halogen free flame retardantInformation provided by LANXESS.
Physical Properties Metric English Comments
Density 1.275 g/cc
0.04606 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.8 %
1.8 %
50% RH; ISO 62
Water Absorption at Saturation 5.5 %
5.5 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
60x60x2; 270°C / WZ 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
60x60x2; 270°C / WZ 80°C; 600 bar; ISO 294-4
Melt Flow 31.8 g/10 min

@Load 2.16 kg,
Temperature 270 °C
 31.8 g/10 min

@Load 4.76 lb,
Temperature 518 °F
 ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
conditioned, 5 mm/min; ISO 527-1,-2
90.0 MPa
13100 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 3.3 %
3.3 %
5 mm/min; ISO 527-1,-2
5.5 %
5.5 %
conditioned, 5 mm/min; ISO 527-1,-2
Tensile Modulus 3.60 GPa
522 ksi
conditioned, 1 mm/min; ISO 527-1,-2
6.50 GPa
943 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 90.0 MPa
13100 psi
conditioned, 2 mm/min; ISO 178-A
150 MPa
21800 psi
2 mm/min; ISO 178-A
Flexural Modulus 3.30 GPa
479 ksi
conditioned, 2 mm/min; ISO 178-A
6.40 GPa
928 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
40.0 kJ/m²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1U
Charpy Impact Unnotched 4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 179-1eU
Thermal Properties Metric English Comments
Melting Point 262 °C
504 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 245 °C
473 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1,-2
Vicat Softening Point 225 °C
437 °F
50 N; 120 °C/h; ISO 306
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
Glow Wire Test 960 °C

@Thickness 0.400 mm
 1760 °F

@Thickness 0.0157 in
 IEC 60695-2-12
960 °C

@Thickness 0.750 mm
 1760 °F

@Thickness 0.0295 in
 IEC 60695-2-12
960 °C

@Thickness 1.50 mm
 1760 °F

@Thickness 0.0591 in
 IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 IEC 60695-2-12
Shrinkage 0.100 %

@Temperature 120 °C,
Time 14400 sec
 0.100 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, 60x60x2; ISO 294-4
0.100 %

@Temperature 120 °C,
Time 14400 sec
 0.100 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, transverse, 60x60x2; ISO 294-4
Electrical Properties Metric English Comments
Comparative Tracking Index >= 600 V
>= 600 V
Solution A; UL 746A
Processing Properties Metric English Comments
Melt Temperature 270 °C
518 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 2.00 - 6.00 hour

@Temperature 80.0 °C
 2.00 - 6.00 hour

@Temperature 176 °F
Moisture Content 0.030 - 0.070 %
0.030 - 0.070 %
residual; Karl Fischer test