Lanxess Durethan® BKV 215 H2.0 901510 Copolyamide, 15% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 215 H2.0 901510 Copolyamide, 15% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CoPA, injection molding grade, 15% glass fibers, elastomer-modified, higher impact and notched impact strength and also higher energy absorption under biaxial impact load than BKV 115, conditioning may be unnecessary in single cases, good heat-ageing resistanceApplication Examples: window surrounds
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Water Absorption 7.0 %
7.0 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 2.0 %
2.0 %
23°C/50% R.H.; Test Sim. to ISO 62
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Conditioned; ISO 527-1/-2
85.0 MPa
12300 psi
ISO 527-1/-2
Elongation at Break 4.5 %
4.5 %
ISO 527-1/-2
15 %
15 %
Conditioned; ISO 527-1/-2
Tensile Modulus 2.40 GPa
348 ksi
Conditioned; ISO 527-1/-2
4.50 GPa
653 ksi
ISO 527-1/-2
Charpy Impact Unnotched 7.00 J/cm²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eU
8.50 J/cm²

@Temperature 23.0 °C
40.4 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.20 J/cm²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
3.50 J/cm²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eA
Impact 1438
1438
Puncture maximum force (N); ISO 6603-2
775

@Temperature -30.0 °C
775

@Temperature -22.0 °F
Puncture maximum force (N); ISO 6603-2
Puncture Energy 11.0 J
8.11 ft-lb
ISO 6603-2
4.50 J

@Temperature -30.0 °C
3.32 ft-lb

@Temperature -22.0 °F
ISO 6603-2
4.50 J

@Temperature -30.0 °C
3.32 ft-lb

@Temperature -22.0 °F
Conditioned; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 150 µm/m-°C
83.3 µin/in-°F
ISO 11359-1/-2
Melting Point 213 °C
415 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 60.0 °C
140 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
IEC 60695-11-10
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Descriptive Properties Value Comments
Features Heat stabilized or stable to heat
High impact or high impact modified
Form Pellets
ISO Shortname ISO 1874-PA 6/66-HI,MHR,-050,GF15
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America