Lanxess Durethan® BKV 30 H2.0 EF 000000 Nylon 6, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 30 H2.0 EF 000000 Nylon 6, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 30% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ISO 1183
Bulk Density 0.600 g/cc
0.0217 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0020 cm/cm
0.0020 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0070 cm/cm
0.0070 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
cond.; ISO 527-1, -2; 5 mm/min
175 MPa
25400 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 3.4 %
3.4 %
d.a.m.; ISO 527-1, -2; 5 mm/min
4.5 %
4.5 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 5.50 GPa
798 ksi
cond.; ISO 527-1, -2; 1 mm/min
10.0 GPa
1450 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 160 MPa

@Strain 5.00 %
 23200 psi

@Strain 5.00 %
 cond., 2 mm/min; ISO 178-A
260 MPa

@Strain 4.00 %
 37700 psi

@Strain 4.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 140 MPa

@Strain 3.50 %
 20300 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
250 MPa

@Strain 3.50 %
 36300 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 5.50 GPa
798 ksi
cond., 2 mm/min; ISO 178-A
8.50 GPa
1230 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
d.a.m.; ISO 180-1A
15.0 kJ/m²
7.14 ft-lb/in²
cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
70.0 kJ/m²

@Temperature 23.0 °C
 33.3 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
80.0 kJ/m²

@Temperature 23.0 °C
 38.1 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1U
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
7.50 J/cm²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
8.50 J/cm²

@Temperature 23.0 °C
 40.4 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 11.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 219 °C
426 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 204 °C
399 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Melt Temperature 250 - 290 °C
482 - 554 °F
270 °C
518 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GHR, 10-090, GF30