Lanxess Durethan® BKV 50 H2.0 EF DUS30 901510 Nylon 6, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 50 H2.0 EF DUS30 901510 Nylon 6, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 50% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.57 g/cc
1.57 g/cc
ISO 1183
Bulk Density 0.700 g/cc
0.0253 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.00040 cm/cm
0.00040 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0021 cm/cm
0.0021 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.00090 cm/cm
0.00090 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0059 cm/cm
0.0059 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 215 MPa
31200 psi
ISO 527-1, -2; 5 mm/min
Elongation at Break 2.5 %
2.5 %
ISO 527-1, -2; 5 mm/min
Tensile Modulus 16.0 GPa
2320 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 320 MPa

@Strain 3.00 %
46400 psi

@Strain 3.00 %
d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 15.0 GPa
2180 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
d.a.m.; ISO 180-1A
15.0 kJ/m²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
d.a.m.; ISO 180-1A
Izod Impact, Unnotched (ISO) 80.0 kJ/m²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
d.a.m.; ISO 180-1U
80.0 kJ/m²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
d.a.m.; ISO 180-1U
Charpy Impact Unnotched 9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
d.a.m.; ISO 179-1eU
9.00 J/cm²

@Temperature -30.0 °C
42.8 ft-lb/in²

@Temperature -22.0 °F
d.a.m.; ISO 179-1eU
Puncture Energy 3.50 J

@Load <=91.8 kg,
Temperature -30.0 °C
2.58 ft-lb

@Load <=202 lb,
Temperature -22.0 °F
d.a.m.; ISO 6603-2
3.70 J

@Load <=102 kg,
Temperature 23.0 °C
2.73 ft-lb

@Load <=225 lb,
Temperature 73.4 °F
d.a.m.; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1, -2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1, -2
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 213 °C
415 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
280 °C
536 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GHR, 10-160, GF50