- Lanxess Durethan® DP AKV 35 LT H2.0 904040 Nylon 66, 35% Glass Fiber
Lanxess Durethan® DP AKV 35 LT H2.0 904040 Nylon 66, 35% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP AKV 35 LT H2.0 904040 Nylon 66, 35% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding grade, 35% glass fibers, black colored for laser transmission- welding (laser-transparent), good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0031 cm/cm | 0.0031 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0068 cm/cm | 0.0068 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119 MPa | 17300 psi | Conditioned; ISO 527-1/-2 |
| 192 MPa | 27800 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 5.7 % | 5.7 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 7.50 GPa | 1090 ksi | Conditioned; ISO 527-1/-2 |
| 10.8 GPa | 1570 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 2.00 µm/m-°C | 1.11 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 7.00 µm/m-°C | 3.89 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 250 °C | >= 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nylene® NX4747 , 14% Glass Reinforced Translucent Nylon
- Flint Hills 23T2A Random Copolymer Polypropylene
- SABIC Innovative Plastics PC2200 PC (Europe-Africa-Middle East)
- Special Metals INCONEL® Alloy MA 754
- Teknor Apex APEX® 830 Polyvinyl Chloride, Flexible
- Wellman Wellamid® NY-4000 Nylon 6, Engineering Grade
- A. Schulman POLYFORT™ FXP 1227U UV Stable Copolymer Polypropylene
- DuPont™ Fusabond® E100 Polymer Modifier
- Ashley Polymers Ashlene® 520-50G Nylon 66, 50% Glass Reinforced
- BCC Products BC 84 PVA Parting
Copyright © lookpolymers.com All Rights Reserved