Lanxess Pocan® A 3122 901510 PBT+ASA, 20% Glass Fiber

Category Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced
Manufacturer Lanxess
Trade Name Pocan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® A 3122 901510 PBT+ASA, 20% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT + ASA, 20% glass fibers, injection molding, low tendency to warp, improved surface finishInformation provided by LANXESS.
Physical Properties Metric English Comments
Bulk Density 0.700 g/cc
0.0253 lb/in³
ISO 60
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
60x60x2; 270°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
60x60x2; 270°C / MT 80°C; 600 bar; ISO 294-4
Melt Flow 30.8 g/10 min

@Load 2.16 kg,
Temperature 270 °C
30.8 g/10 min

@Load 4.76 lb,
Temperature 518 °F
ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 2.9 %
2.9 %
5 mm/min; ISO 527-1,-2
3.2 %
3.2 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 6.50 GPa
943 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 165 MPa
23900 psi
2 mm/min; ISO 178-A
Flexural Modulus 6.20 GPa
899 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 180-1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
ISO 180-1U
45.0 kJ/m²

@Temperature 23.0 °C
21.4 ft-lb/in²

@Temperature 73.4 °F
ISO 180-1U
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
ISO 179-1eU
5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179-1eA
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
ISO 75-1,-2
Vicat Softening Point 170 °C
338 °F
50 N; 50 °C/h; ISO 306
Shrinkage 0.100 %

@Temperature 120 °C,
Time 14400 sec
0.100 %

@Temperature 248 °F,
Time 4.00 hour
post-shrinkage, transverse, 60x60x2; ISO 294-4
0.200 %

@Temperature 120 °C,
Time 14400 sec
0.200 %

@Temperature 248 °F,
Time 4.00 hour
post-shrinkage, 60x60x2; ISO 294-4
Processing Properties Metric English Comments
Melt Temperature 270 °C
518 °F
Injection molding; ISO 294
Mold Temperature 90.0 °C
194 °F
Injection molding; ISO 294
Dry Time 4.00 - 8.00 hour

@Temperature 120 °C
4.00 - 8.00 hour

@Temperature 248 °F
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
Karl Fischer test