Lanxess Pocan® DP C 1502 000000 PBT + PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® DP C 1502 000000 PBT + PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT + PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | 60x60x2; 250°C / WZ 70°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | 60x60x2; 250°C / WZ 70°C; 600 bar; ISO 294-4 |
| Melt Flow | 35 g/10 min @Load 5.00 kg, Temperature 270 °C |
35 g/10 min @Load 11.0 lb, Temperature 518 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1, -2; 50 mm/min |
| Elongation at Break | >= 40 % | >= 40 % | ISO 527-1, -2; 50 mm/min |
| Elongation at Yield | 3.8 % | 3.8 % | ISO 527-1, -2; 50 mm/min |
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 75.0 MPa @Strain 5.50 % |
10900 psi @Strain 5.50 % |
2 mm/min; ISO 178-A |
| Flexural Yield Strength | 65.0 MPa @Strain 3.50 % |
9430 psi @Strain 3.50 % |
2 mm/min; ISO 178-A |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180-1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 180-1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | 1.90 J/cm² @Temperature -30.0 °C |
9.04 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1, -2 |
| Vicat Softening Point | 125 °C @Load 5.10 kg |
257 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| Glow Wire Test | 750 °C @Diameter 4.00 mm |
1380 °F @Diameter 0.157 in |
GWFI; IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | for test specimens; ISO 294 |
| 250 - 265 °C | 482 - 509 °F | ||
| Mold Temperature | 70.0 °C | 158 °F | for test specimens; ISO 294 |
| 60.0 - 90.0 °C | 140 - 194 °F | ||
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4 - 8 hour | 4 - 8 hour | |
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 7792-1-PBT+PC, GHLMPR, 11-020 |