Lanxess Pocan® S 7020 000000 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Extrusion Grade , Polybutylene Terephthalate (PBT), Flame Retardant , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer Lanxess
Trade Name Pocan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® S 7020 000000 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, non-reinforced, injection molding, extrusion, flame retardant, impact modified
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
Water Absorption 0.60 %
0.60 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; Test Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0017 cm/cm
0.0017 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0017 cm/cm
0.0017 in/in
ISO 294-4, 2577
Melt Flow 49 g/10 min

@Load 5.00 kg,
Temperature 270 °C
49 g/10 min

@Load 11.0 lb,
Temperature 518 °F
Calculated from MVR using melt density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 34.0 MPa
4930 psi
ISO 527-1/-2
Tensile Strength, Yield 45.0 MPa
6530 psi
ISO 527-1/-2
Elongation at Break 10 %
10 %
ISO 527-1/-2
Elongation at Yield 3.0 %
3.0 %
ISO 527-1/-2
Tensile Modulus 2.40 GPa
348 ksi
ISO 527-1/-2
Charpy Impact Unnotched 12.0 J/cm²

@Temperature -30.0 °C
57.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 2300 MPa
334000 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 1600 MPa
232000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 46.0 °C
115 °F
ISO 75-1/-2
Vicat Softening Point 160 °C
320 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-2

@Thickness 0.800 mm
V-2

@Thickness 0.0315 in
IEC 60695-11-10
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
IEC 60695-11-10
Oxygen Index 30 %
30 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+17 ohm-cm
>= 1.00e+17 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
IEC 60250
3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
IEC 60250
Dielectric Strength 23.0 kV/mm
584 kV/in
IEC 60243-1
Dissipation Factor 0.0040

@Frequency 100 Hz
0.0040

@Frequency 100 Hz
IEC 60250
0.024

@Frequency 1.00e+6 Hz
0.024

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 10724
Descriptive Properties Value Comments
Additives Flame retarding agent
Release agent
Features Flame retardant
High impact or high impact modified
Form Pellets
ISO Shortname ISO 7792-1-PBT,GFHMPR,11-020; ISO 1043-PBT FR(17)
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America