Lavergne VYPET VNT 215 PET - PBT 15% Glass Reinforced Polyester
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | Lavergne Performance Compounds |
| Trade Name | VYPET |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lavergne VYPET VNT 215 PET - PBT 15% Glass Reinforced Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vypet VNT 215 is a 15% fiberglass reinforced PET/PBT injection molding compound designed for structural applications.Features: High temperature performance; Low warp; High quality surfaceTypical Applications: Office equipment; AppliancesInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm |
0.0040 in/in @Thickness 0.0787 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm |
0.010 in/in @Thickness 0.0787 in |
ASTM D955 |
| Ash | 15 % | 15 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 130 MPa | 18900 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.550 J/cm @Temperature 23.0 °C |
1.03 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 275 °C | 518 - 527 °F | |
| Front Barrel Temperature | 275 - 280 °C | 527 - 536 °F | |
| Nozzle Temperature | 275 - 290 °C | 527 - 554 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | |
| Mold Temperature | 75.0 - 100 °C | 167 - 212 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi |
Users viewing this material also viewed the following:
- Polymer Industries Densetec HDPE Sheet
- Indium Corp. 99.99% InF3 Indium Trifluoride, Anhydrous
- Ineos G60-25-144 HDPE
- Kazanorgsintez 108-278 Low Density Polyethylene Composition with Improved Processibility
- Saint-Gobain Chemlam® 3320 High Mechanical Performance Industrial Laminate
- Saint-Gobain Chemfab® 3 Tear Resistant PTFE-Coated Glass
- Chem Polymer Chemlon 212 Nylon 6, Lubricated, GP
- Formosa Plastics Formolene® 6375N Impact Copolymer Polypropylene
- Overview of materials for Polyethylene Terephthalate (PET), Glass/Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved