Lavergne VYPET VNT 615 FR PET 15% Glass Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant
Manufacturer Lavergne Performance Compounds
Trade Name VYPET
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lavergne VYPET VNT 615 FR PET 15% Glass Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vypet VNT 615 FR is a 15% fiberglass reinforced flame retardant PET injection molding compound designed for electrical and structural applications.Features: Flame retardant; UL yellow card file E216152; Excellent strength and stiffness; Excellent dimensional stabilityTypical Applications: Electrical parts; Appliances; Electronic applicationsInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Thickness 2.00 mm
0.0040 in/in

@Thickness 0.0787 in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0090 cm/cm

@Thickness 2.00 mm
0.0090 in/in

@Thickness 0.0787 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
5 mm/min; ASTM D638
Flexural Strength 155 MPa
22500 psi
1.3 mm/min; ASTM D790
Flexural Modulus 5.90 GPa
856 ksi
1.3 mm/min; ASTM D790
Izod Impact, Notched 0.700 J/cm

@Temperature 23.0 °C
1.31 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.850 mm
V-0

@Thickness 0.0335 in
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
Glow Wire Test 900 °C
1650 °F
GWIT at 1.0 mm; IEC 60695-2-13
960 °C
1760 °F
GWFI at 1.0 mm; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+18 ohm-cm
1.00e+18 ohm-cm
ASTM D257
Dielectric Strength 37.0 kV/mm
940 kV/in
ASTM D149
Comparative Tracking Index 0.00 - 15 V
0.00 - 15 V
UL746
Processing Properties Metric English Comments
Feed Temperature 260 - 270 °C
500 - 518 °F
Middle Barrel Temperature 265 - 275 °C
509 - 527 °F
Front Barrel Temperature 270 - 290 °C
518 - 554 °F
Nozzle Temperature 275 - 295 °C
527 - 563 °F
Melt Temperature 275 - 295 °C
527 - 563 °F
Mold Temperature 95.0 - 120 °C
203 - 248 °F
Injection Pressure 55.0 - 85.0 MPa
7980 - 12300 psi