- Lehmann & Voss LUVOCOM® 1105-0904/GN PEEK, with glass fiber
Lehmann & Voss LUVOCOM® 1105-0904/GN PEEK, with glass fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-0904/GN PEEK, with glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.High dimensionally stable precision parts, high continuous use temperature.Suitable for biocompatible application, superheated steam sterilizable.High chemical resistance parts, hydrolysis resistance, non flammable.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 150 MPa | 21800 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.5 % | 2.5 % | flexural | |
| Modulus of Elasticity | 11.0 GPa | 1600 ksi | |
| Flexural Strength | 210 MPa | 30500 psi | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | flatwise; ISO 179 1fU |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | |
| Coefficient of Friction, Static | 0.30 | 0.30 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 22.0 µm/m-°C | 12.2 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 280 °C | 536 °F | short term | |
| Vicat Softening Point | 325 °C | 617 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | turquoise green |
Users viewing this material also viewed the following:
- Osprey Metals D2 Tool Steel Powder (Grade 95% - 16)
- LG Chemical LUPOY GN1004FA PC, Halogen Free, Flame Retardant, Chemical Resistance
- Gromax BTE35-DN00N1 Nylon 6 (Conditioned)
- Solvay Specialty Polymers Tecnoflon® PFR 94 Perfluoroelastomer
- SABIC Innovative Plastics LNP STAT-KON RE004 PA 66
- Styron DL 380 Carboxylated SB
- CTC X-PRO CTC PP1020 Polypropylene Homopolymer
- Axiall 8610 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved