- Lehmann & Voss LUVOCOM® 1500-8299 Polysulfone, with PTFE, lubricant modified
Lehmann & Voss LUVOCOM® 1500-8299 Polysulfone, with PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone with PTFE/Silicone Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1500-8299 Polysulfone, with PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Control disks, cams, sliding elements and other duty parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0060 - 0.012 cm/cm | 0.0060 - 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 56.0 MPa | 8120 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.7 % | 6.7 % | flexural | |
| Modulus of Elasticity | 2.10 GPa | 305 ksi | |
| Flexural Strength | 80.0 MPa | 11600 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 µm/m-°C | 30.6 µin/in-°F | DIN 53752 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 170 °C | 338 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 355 °C | 671 °F | mass temp |
| Nozzle Temperature | 350 - 370 °C | 662 - 698 °F | |
| Zone 1 | 340 - 360 °C | 644 - 680 °F | |
| Zone 2 | 345 - 365 °C | 653 - 689 °F | |
| Zone 3 | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 140 - 170 °C | 284 - 338 °F | |
| Drying Temperature | 140 °C @Time 10800 - 14400 sec |
284 °F @Time 3.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (beige) |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® ESD 5400
- SABIC Innovative Plastics Lexan® SLX1432D PC Copolymer (Asia Pacific)
- Solvay Specialty Polymers Udel® P-1750 MR Polysulfone (PSU) (Unverified Data**)
- Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (Conditioned), Injection Molding Grade
- Hexcel® HexPly® 954-2A Curing Cyanate Resin, S-2 Glass Fiber Reinforced 8 Harness Satin Fabric
- Lubrizol ESTANE® 58881 Ether Based Thermoplastic Polyurethane
- Polyplastics Duranex® 3300 Polybutylene Terephthalate (PBT), Standard, 30% GF filled
- Aclo Accutech Polypropylene Homopolymer HP0336M10CL Mica Reinforced Coupled
Copyright © lookpolymers.com All Rights Reserved