Lotte Chemical Titan TITANLENE® LDF200YZ Low density polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade
Manufacturer Lotte Chemical Titan Holding Sdn. Bhd. (Former Titan Chemicals)
Trade Name TITANLENE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lotte Chemical Titan TITANLENE® LDF200YZ Low density polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LDF200YZ is a low density polyethylene resin for film extrusion. LDF200YZ has no slip and anti-block additives. LDF200YZ meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2.Applications: T-shirt bags Display packaging Light duty shrink filmAdditives: BarefootAdvantages: Good optical Good mechanical propertiesInformation provided by Titan Chemicals
Physical Properties Metric English Comments
Base Resin Density 0.922 g/cc
0.0333 lb/in³
ASTM D1505
Thickness 30.0 microns
1.18 mil
extruded at 2.5:1 BUR
Base Resin Melt Index 2.0 g/10 min
2.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 310 %
310 %
ASTM D882
Film Elongation at Break, TD 580 %
580 %
ASTM D882
Elmendorf Tear Strength, MD 6.00 g/micron
152 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 4.00 g/micron
102 g/mil
ASTM D1922
Dart Drop 2.00 g/micron
50.8 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 26.5 MPa
3840 psi
ASTM D882
Film Tensile Strength at Break, TD 21.6 MPa
3130 psi
ASTM D882
1% Secant Modulus, MD 205.94 MPa
29869 psi
ASTM D882
1% Secant Modulus, TD 225.56 MPa
32714 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 95.0 °C
203 °F
resin; ASTM D1525
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Processing Properties Metric English Comments
Melt Temperature 160 - 180 °C
320 - 356 °F
Blow-up Ratio (BUR) 2.5
2.5