- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyurethane, TP
- Thermoplastic Polyurethane (TPUR), Polyester Grade
- Lubrizol Advanced Materials PEARLTHANE® Clear 15N80 Thermoplastic Polyurethane Elastomer
Lubrizol Advanced Materials PEARLTHANE® Clear 15N80 Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlthane® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials PEARLTHANE® Clear 15N80 Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PEARLTHANE® CLEAR 15N80 is a polyether copolymer-based TPU, supplied in form of translucent, colorless, combining low hardness with excellent mechanical properties and excellent hydrolysis resistance. It can be extruded and injection-molded.All information provided by Merquinsa
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 21.6 kg |
10 g/10 min @Load 47.6 lb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 82 | 82 | ASTM D2240 |
| Tensile Strength, Yield | 35.00 MPa | 5076 psi | ASTM D412 |
| Elongation at Break | 740 % | 740 % | ASTM D412 |
| 100% Modulus | 0.00500 GPa | 0.725 ksi | ASTM D412 |
| 300% Modulus | 0.00800 GPa | 1.16 ksi | ASTM D412 |
| Tear Strength | 80.6 kN/m | 460 pli | ASTM D624 (Die C) |
| Abrasion | 25 | 25 | loss (mm³); DIN 53.516 |
| Compression Set | 24 % @Temperature 22.8 °C, Time 252000 sec |
24 % @Temperature 73.0 °F, Time 70.0 hour |
ASTM D395 |
| 38 % @Temperature 70.0 °C, Time 86400 sec |
38 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 196 - 204 °C | 385 - 400 °F | MQSA 111 |
| Glass Transition Temp, Tg | -53.9 °C | -65.0 °F | DSC, 10ºC/min; DIN 51.007 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 185 °C | 365 °F | |
| Nozzle Temperature | 199 °C | 390 °F | |
| Zone 1 | 191 °C | 375 °F | Compression Zone |
| Zone 2 | 196 °C | 385 °F | Metering Zone |
| Mold Temperature | 35.0 °C | 95.0 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % | MQSA 44 |
| Injection Pressure | 10.0 MPa | 1450 psi | |
| Hold Pressure | 4.83 MPa @Time 10.0 sec |
700 psi @Time 0.00278 hour |
|
| Cycle Time - Injection | 4.0 sec | 4.0 sec | |
| Cycle Time - Cooling | 30 sec | 30 sec | |
| Screw Speed | 142 rpm | 142 rpm |
Users viewing this material also viewed the following:
- Polykemi AB SCANBLEND FS8 ASUV4 PC/ASA, Antistatic, Improved Weather Resistance
- Kleerdex Vinyloy™ 102 Acrylic/PVC Thermoplastic Sheet (discontinued **)
- Gromax BTE30-FN00N1 Nylon 6 (Dry)
- Borealis Borecene™ RM8403 Linear Polyethylene for Rotational Molding
- EMS-Griltech Griltex® D 1531E Copolyester Hotmelt Adhesive (Technical Applications)
- CLAL-MSX SICLANIC S® TD3 Quenched Copper Alloy, 1/2 Hard
- 3M Scotchcal™ ElectroCut™ 7725-63 Graphic Film
- ConocoPhillips Hydroclear Diamond Class® 100 Turbine Oil
- Arkema Group Oroglas® VM Acrylic, Injection Molding Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved