Lubrizol ESTALOC® 59300 Ester-Type, Reinforced Engineering Thermoplastic (European Grade)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Glass Filled
Manufacturer Lubrizol (former Noveon)
Trade Name ESTALOC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol ESTALOC® 59300 Ester-Type, Reinforced Engineering Thermoplastic (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Estaloc® RETP (Reinforced Engineering Thermoplastic) is a tough, dimensionally stable, abrasion-resistant thermoplastic that withstands demanding environments. Developed as an extension to the Noveon Estane® TPU technology, Estaloc® RETP products complement Estane's durability and aesthetics with increased stiffness capability and dimensional stability over a broad temperature performance range not available from other engineering thermoplastics.Major Benefits of Estaloc® RETPs: Superior Dimensional Stability approaching that of metalsClass A surface aestheticsPaintability with no primer nor adhesion promoterExcellent abrasion and scuff/mar resistance Toughness over a broad temperature rangeExcellent adhesion to a variety of overmolding chemistriesSpecific Notes for this Material: Fiberglass reinforced TPU - industry standard for recreational wheel hubs Information provided by Noveon, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ISO 1183
Filler Content 30 %
30 %
Linear Mold Shrinkage 0.0015 cm/cm
0.0015 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore D 72
72
ISO 868
Tensile Strength, Ultimate 78.0 MPa
11300 psi
ISO 527-2/1A/5
Elongation at Break 15 %
15 %
ISO 527-2/1A/5
Tensile Modulus 3.636 GPa
527.4 ksi
ISO 527-2/1A/1
Flexural Strength 77.0 MPa
11200 psi
ISO 178
Flexural Modulus 3.20 GPa
464 ksi
ISO 178
Izod Impact, Notched (ISO) 17.0 kJ/m²
8.09 ft-lb/in²
Low Temp; ISO 180/1eA
48.0 kJ/m²
22.8 ft-lb/in²
ISO 180/1eA
Izod Impact, Unnotched (ISO) 117 kJ/m²
55.7 ft-lb/in²
ISO 180/1eU
73.0 kJ/m²

@Temperature -30.0 °C
34.7 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1eU
Charpy Impact Unnotched 12.2 J/cm²
58.1 ft-lb/in²
ISO 179/1eU
70.0 J/cm²

@Temperature -30.0 °C
333 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 4.90 J/cm²
23.3 ft-lb/in²
ISO 179/1eA
11.5 J/cm²

@Temperature -30.0 °C
54.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 20
20
CS-17 wheel; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear 18.0 µm/m-°C

@Temperature 20.0 °C
10.0 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
method Bf; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
method Af; ISO 75-2
Vicat Softening Point 116 °C
241 °F
temperature B; ISO 36
175 °C
347 °F
temperature A; ISO 306