Lubrizol Estane® 2103-90AENH Film Grade Thermoplastic Polyurethane Elastomer

Category Polymer , Film , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® 2103-90AENH Film Grade Thermoplastic Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formerly PellethaneFeature: NSF Standard 61 Certified, FDA ComplianceAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by Lubrizol.Lubrizol acquired the Pellethane product line from Dow in 2009.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Melt Flow 9.0 g/10 min

@Load 8.70 kg,
Temperature 224 °C
9.0 g/10 min

@Load 19.2 lb,
Temperature 435 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 90
90
ASTM D2240
Hardness, Shore D 47
47
ASTM D2240
Tensile Strength, Ultimate 48.2 MPa
6990 psi
ASTM D412
Elongation at Break 560 %
560 %
ASTM D412
50% Modulus 0.00620 GPa
0.899 ksi
ASTM D412
100% Modulus 0.00900 GPa
1.31 ksi
ASTM D412
300% Modulus 0.0172 GPa
2.49 ksi
ASTM D412
Tear Strength 126 kN/m
719 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 50
50
H-22 wheel (coarser), 1000g; ASTM D1044
Compression Set 25 %
25 %
22 hrs. @ 77°F (25°C); ASTM D395, Method B
40 %

@Temperature 70.0 °C
40 %

@Temperature 158 °F
22 hrs.; ASTM D395, Method B
Tensile Set 60 %
60 %
Elongation Set After Break; ASTM D412
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 155 µm/m-°C

@Temperature 20.0 °C
86.1 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Vicat Softening Point 90.0 °C
194 °F
120°C/hr, 9.8N; ASTM D1525
Glass Transition Temp, Tg -34.0 °C
-29.2 °F
DSC
Processing Properties Metric English Comments
Melt Temperature 188 - 204 °C
370 - 399 °F
Extrusion
193 - 210 °C
379 - 410 °F
Molding
Mold Temperature 16.0 - 60.0 °C
60.8 - 140 °F
Drying Temperature 88.0 - 104 °C
190 - 219 °F
air dew point <-40°C