Lubrizol Estane® CP80AS2 Thermoplastic Polyurethane

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® CP80AS2 Thermoplastic Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Type: Estane® CP80AS2 is a soft, polyester based thermoplastic polyurethane resin.Features: Outstanding compatibility with flexible PVC allowing easy dispersion without pre-compounding.Uses: Tube/Hose and Sheet Extrusion, Wire/CableAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation Provided by The Lubrizol Corporation
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D792
1.15 g/cc
1.15 g/cc
PVC (80)/CP80AS2(20)
1.15 g/cc
1.15 g/cc
PVC (70)/CP80AS2(30)
1.15 g/cc
1.15 g/cc
PVC (50)/CP80AS2(50)
Maximum Moisture Content 0.020
0.020
Mechanical Properties Metric English Comments
Hardness, Shore A 62
62
PVC (80)/CP80AS2(20)
63
63
PVC (70)/CP80AS2(30)
65
65
PVC (50)/CP80AS2(50)
81

@Time 5.00 sec
81

@Time 0.00139 hour
ASTM D2240
Tensile Strength at Break 15.9 MPa
2310 psi
PVC (80)/CP80AS2(20)
18.6 MPa
2700 psi
PVC (70)/CP80AS2(30)
24.1 MPa
3500 psi
PVC (50)/CP80AS2(50)
Tensile Strength, Ultimate 27.6 MPa
4000 psi
ASTM D412
Elongation at Break 470 %
470 %
ASTM D412
540 %
540 %
PVC (80)/CP80AS2(20)
580 %
580 %
PVC (70)/CP80AS2(30)
665 %
665 %
PVC (50)/CP80AS2(50)
100% Modulus 0.00390 GPa
0.566 ksi
ASTM D412
300% Modulus 0.00840 GPa
1.22 ksi
ASTM D412
Flexural Modulus 0.00383 GPa
0.555 ksi
PVC (80)/CP80AS2(20)
0.00434 GPa
0.630 ksi
PVC (70)/CP80AS2(30)
0.00579 GPa
0.840 ksi
PVC (50)/CP80AS2(50)
Tear Strength 5.43 kN/m
31.0 pli
Trouser, PVC (80)/CP80AS2(20)
7.01 kN/m
40.0 pli
Trouser, PVC (70)/CP80AS2(30)
11.7 kN/m
67.0 pli
Trouser, PVC (50)/CP80AS2(50)
21.9 kN/m
125 pli
Trouser; ASTM D470
Graves Tear Strength 29.8 kN/m
170 pli
PVC (80)/CP80AS2(20)
33.3 kN/m
190 pli
PVC (70)/CP80AS2(30)
47.3 kN/m
270 pli
PVC (50)/CP80AS2(50)
63.1 kN/m
360 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 86
86
PVC (50)/CP80AS2(50)
128
128
PVC (70)/CP80AS2(30)
146
146
PVC (80)/CP80AS2(20)
14

@Load 1.00 kg
14

@Load 2.20 lb
H-18 wheel; ASTM D3389
Abrasion 83
83
[mm<sup>3</sup>], PVC (50)/CP80AS2(50)
126
126
[mm<sup>3</sup>], PVC (70)/CP80AS2(30)
148
148
[mm<sup>3</sup>], PVC (80)/CP80AS2(20)
Compression Set 13 %
13 %
PVC (80)/CP80AS2(20)
16 %
16 %
PVC (70)/CP80AS2(30)
19 %
19 %
PVC (50)/CP80AS2(50)
Tensile Set 14 %
14 %
PVC (50)/CP80AS2(50)
16 %
16 %
PVC (70)/CP80AS2(30)
19 %
19 %
PVC (80)/CP80AS2(20)
Thermal Properties Metric English Comments
Melting Point 140 °C
284 °F
DSC
Glass Transition Temp, Tg -30.0 °C
-22.0 °F
DSC
Processing Properties Metric English Comments
Zone 1 170 °C
338 °F
Extrusion
Zone 2 175 °C
347 °F
Extrusion
Zone 3 180 °C
356 °F
Extrusion
Zone 4 180 °C
356 °F
Extrusion
Adapter Temperature 180 °C
356 °F
5, Extrusion
Die Temperature 180 °C
356 °F
6, Zone 1, Extrusion
180 °C
356 °F
Zone 2, Extrusion
Drying Temperature 150 °C
302 °F
overnight
Dew Point -40.0 °C
-40.0 °F