Lubrizol Estane® ZHF 90AT0 Thermoplastic Polyurethane, Flame Retardant

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyether Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® ZHF 90AT0 Thermoplastic Polyurethane, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Type: Estane® ZHF 90AT0 TPU is a clear, glossy, zero halogen flame retardant polyether based thermoplastic polyurethane compound.Features: Outstanding TPU properties.Uses: Cable jacket and tube/hose and injection molding and fabric coatingAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation Provided by The Lubrizol Corporation
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Mechanical Properties Metric English Comments
Hardness, Shore A 91

@Time 5.00 sec
91

@Time 0.00139 hour
ASTM D2240
Tensile Strength, Ultimate 46.5 MPa
6750 psi
ASTM D412
Elongation at Break 400 %
400 %
ASTM D412
100% Modulus 0.0100 GPa
1.45 ksi
ASTM D412
300% Modulus 0.0290 GPa
4.21 ksi
ASTM D412
Tear Strength 25.2 kN/m
144 pli
Trouser; ASTM D470
Graves Tear Strength 102 kN/m
583 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 54

@Load 1.00 kg
54

@Load 2.20 lb
H-18 wheel; ASTM D3389
Thermal Properties Metric English Comments
Melting Point 172 °C
342 °F
DSC
Glass Transition Temp, Tg -38.0 °C
-36.4 °F
DSC
Flammability, UL94 V-2

@Thickness 0.762 mm
V-2

@Thickness 0.0300 in
Vertical Flame Test; ASTM D3801
Processing Properties Metric English Comments
Zone 1 180 °C
356 °F
Extrusion
180 °C
356 °F
Extrusion
Zone 2 185 °C
365 °F
Extrusion
185 °C
365 °F
Extrusion
Zone 3 190 °C
374 °F
Extrusion
190 °C
374 °F
Extrusion
Zone 4 195 °C
383 °F
Extrusion
195 °C
383 °F
Extrusion
Adapter Temperature 195 °C
383 °F
5, Extrusion
Die Temperature 205 °C
401 °F
6, Zone 1, Extrusion
205 °C
401 °F
Zone 2, Extrusion
Drying Temperature 180 °C
356 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Dew Point -40.0 °C
-40.0 °F
Descriptive Properties Value Comments
RT Burst Pressure 4.3 MPa
ISO 7628/1