Lubrizol ISOPLAST™ 2560 Engineering Thermoplastic Polyurethane Resin for Medical Applications

Category Polymer , Thermoplastic , Polyurethane, TP
Manufacturer Lubrizol (former Noveon)
Trade Name ISOPLAST™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol ISOPLAST™ 2560 Engineering Thermoplastic Polyurethane Resin for Medical Applications.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaAvailableInformation provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
Physical Properties Metric English Comments
Specific Gravity 1.71 g/cc
1.71 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 228 MPa
33000 psi
ASTM D638
Tensile Strength, Yield 228 MPa
33000 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Elongation at Yield 2.0 %
2.0 %
ASTM D638
Tensile Modulus 17.2 GPa
2500 ksi
ASTM D638
Flexural Strength 393 MPa
57000 psi
ASTM D790
Flexural Modulus 15.2 GPa
2200 ksi
ASTM D790
Izod Impact, Notched 8.54 J/cm

@Thickness 3.17 mm,
Temperature -40.0 °C
16.0 ft-lb/in

@Thickness 0.125 in,
Temperature -40.0 °F
ASTM D256
8.54 J/cm

@Thickness 3.17 mm,
Temperature 22.8 °C
16.0 ft-lb/in

@Thickness 0.125 in,
Temperature 73.0 °F
ASTM D256
Dart Drop, Total Energy 25.0 J

@Temperature -28.9 °C
18.4 ft-lb

@Temperature -20.0 °F
ASTM D3763
29.0 J

@Temperature 22.8 °C
21.4 ft-lb

@Temperature 73.0 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 10.8 µm/m-°C

@Temperature 20.0 °C
6.00 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
260 °F
unannealed; ASTM D648
127 °C
260 °F
annealed; ASTM D648
Vicat Softening Point 186 °C
366 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 238 - 260 °C
460 - 500 °F
Mold Temperature 66.0 - 88.0 °C
151 - 190 °F
Drying Temperature 82.0 - 99.0 °C
180 - 210 °F