Lubrizol Isoplast® 101LGF60NAT Engineering Thermoplastic Polyurethane Resin
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Isoplast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Isoplast® 101LGF60NAT Engineering Thermoplastic Polyurethane Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 227 MPa | 32900 psi | ASTM D638 |
| Tensile Strength, Yield | 227 MPa | 32900 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 17.0 GPa | 2470 ksi | ASTM D638 |
| Flexural Strength | 393 MPa | 57000 psi | ASTM D790 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
| Izod Impact, Unnotched | 8.54 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
16.0 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| 8.54 J/cm @Thickness 81.3 mm, Temperature -40.0 °C |
16.0 ft-lb/in @Thickness 3.20 in, Temperature -40.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 25.0 J @Temperature -29.0 °C |
18.4 ft-lb @Temperature -20.2 °F |
ASTM D3767 |
| 29.0 J @Temperature 23.0 °C |
21.4 ft-lb @Temperature 73.4 °F |
ASTM D3767 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 °C |
6.11 µin/in-°F @Temperature 68.0 °F |
ASTM D 696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Unannealed; ASTM D648 |
| 127 °C | 261 °F | Annealed; ASTM D648 | |
| Vicat Softening Point | 186 °C | 367 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 65.0 - 90.0 °C | 149 - 194 °F | |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F |
Users viewing this material also viewed the following:
- RheTech Products FT3080-81 Thermoplastic Polyolefin, UV Stabilized, ACRA Titanium
- PolyChem Alloy PolyFoam HDC5
- Noble Polymers Regis™ 235107 Thermoplastic Olefin (TPO)
- Resin Technology Group CT-988 Cationic UV Cure Epoxy Adhesive
- SABIC Innovative Plastics Lexan® LC120 PC (Asia Pacific)
- Abatron 85082 A/B Filled Potting Compound (discontinued **)
- Ferro EG 3608 Metal Sealing
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- Engineered Plastics EPPC 1214C Polycarbonate
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction
Copyright © lookpolymers.com All Rights Reserved