LyondellBasell Alathon® M5370PX High Density Polyethylene, Extrusion Grade

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer LyondellBasell (former Equistar)
Trade Name Alathon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Alathon® M5370PX High Density Polyethylene, Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ALATHON M5370PX is a copolymer with a narrow molecular weight distribution. This resin provides high impact strength and stress crack resistance, excellent color, low odor and good processability. Typical applications include pipe and profile extrusion.Regulatory Status: M5370PX meets the requirements of the Food and Drug Administration regulation 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales or technical service representative for more information.This product is from the former Equistar product line.
Physical Properties Metric English Comments
Density 0.953 g/cc
0.0344 lb/in³
ASTM D1505
Melt Flow 6.8 g/10 min
6.8 g/10 min
ASTM D1238
Spiral Flow 24.1 cm
9.50 in
Equistar test
Mechanical Properties Metric English Comments
Hardness, Shore D 67
67
ASTM D2240
Tensile Strength at Break 22.4 MPa
3250 psi
ASTM D638
Tensile Strength, Yield 28.3 MPa
4110 psi
2"/min; ASTM D638
Elongation at Yield 7.3 %
7.3 %
2"/min; ASTM D638
1% Secant Modulus 1250 MPa
181000 psi
0.5"/min; ASTM D790
2% Secant Modulus 1.04 GPa
151 ksi
ASTM D790
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 72.0 °C
162 °F
ASTM D648
Vicat Softening Point 127 °C
261 °F
ASTM D1525
Brittleness Temperature <= -76.0 °C
<= -105 °F
ASTM D746