LyondellBasell Hifaxâ„¢ CA1110/2AC Thermoplastic Polyolefin Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin
Manufacturer	LyondellBasell
Trade Name	Hifax™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Hifaxâ„¢ CA1110/2AC Thermoplastic Polyolefin Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Hifaxâ„¢ CA1110/2AC Black medium high melt flow, 1,200 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has a very good balance of processability, impact resistance and paintability. It was designed primarily for use in painted automotive bumper fascia applications. Uses: Automotive exterior partsInformation provided by Basell.

Physical Properties	Metric	English	Comments
Density	0.990 g/cc	0.0358 lb/inÂ³	ISO 1183
Melt Flow	9.0 g/10 min @Load 2.16 kg, Temperature 230 Â°C	9.0 g/10 min @Load 4.76 lb, Temperature 446 Â°F	Condition L; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	17.0 MPa	2470 psi	ISO 527-1, -2
Elongation at Yield	100 %	100 %	ISO 527-1, -2
Flexural Modulus	1.20 GPa	174 ksi	ISO 178
Izod Impact, Notched (ISO)	8.90 kJ/mÂ² @Temperature -40.0 Â°C	4.24 ft-lb/inÂ² @Temperature -40.0 Â°F	ISO 180
	50.0 kJ/mÂ² @Temperature 23.0 Â°C	23.8 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 180
Multi-axial Impact @ -30Â°C Total Energy	23.0 J	17.0 ft-lb	Energy to Peak Force (-22Â°F, Ductile Failure); ISO 6603-2

Thermal Properties	Metric	English	Comments
CTE, linear	75.0 Âµm/m-Â°C @Temperature -30.0 - 100 Â°C	41.7 Âµin/in-Â°F @Temperature -22.0 - 212 Â°F	ASTM D696
Shrinkage	0.90 %	0.90 %	Tool, Injection Molded 100x150x3.2 mm Plaque; Basell Test Method
	1.00 % @Temperature 121 Â°C, Time 3600 sec	1.00 % @Temperature 250 Â°F, Time 1.00 hour	Afterbake, 100x150x3.2 mm; Basell Method