LyondellBasell Hifaxâ„¢ CB259 Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CB259 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ CB259 medium high melt flow, 1,600 MPa flexural modulus, low CLTE, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good balance of impact resistance, rigidity and dimensional stability. It was designed for exterior ornamentation applications requiring stiffness and low thermal expansion characteristics. Uses: Automotive exterior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C |
13 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 55 | 55 | ISO 2039-2 |
| Hardness, Shore D | 69 | 69 | ISO 868 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527-1, -2 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-1, -2 |
| Elongation at Break | 450 % | 450 % | ISO 527-1, -2 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527-1, -2 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 33.0 kJ/m² @Temperature 23.0 °C |
15.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop, Total Energy | 21.0 J @Temperature -15.0 °C |
15.5 ft-lb @Temperature 5.00 °F |
Instrumented Energy at Maximum Load, Ductile Failure; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 49.0 µm/m-°C @Temperature -30.0 - 100 °C |
27.2 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.9 °C | 201 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 °C | 127 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.50 % | 0.50 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 0.800 % @Temperature 121 °C, Time 3600 sec |
0.800 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREFLEX E50 Polyphenylene Ether (PPO/PPE)
- Lanxess Durethan® BKV 35 H3.0 000000 Nylon 6, Glass Fiber Reinforced
- Teknor Apex Monprene® MP-1646-L3 Thermoplastic Elastomer
- Polyplastics Duranex® HN7315 Polybutylene Terephthalate (PBT), Low warpage, 15% GF filled
- CP-Polymer-Technik Wellamid® 6600 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 66, Heat Stabilized, Conditioned
- Entec Hylox® 9020 PBT, 20% Glass Reinforced
- Braskem GF4960 HDPE Blow Molding Polyethylene Homopolymer
- Permabond MH052 Anaerobic Threadsealant
- ExxonMobil Escorene® LD 728.61 Molding, extrusion and compounding resin
Copyright © lookpolymers.com All Rights Reserved