LyondellBasell Hifaxâ„¢ RTA3263EC/1 Thermoplastic Polyolefin Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin
Manufacturer	LyondellBasell
Trade Name	Hifax™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Hifaxâ„¢ RTA3263EC/1 Thermoplastic Polyolefin Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Hifaxâ„¢ RTA3263EC/1 fractional melt flow, 1,700 MPa flexural modulus, mineral-filled, extrusion grade thermoplastic elastomeric olefin (TEO) resin has an excellent balance of stiffness, impact strength and processability. It was designed primarily for extruded automotive exterior profile applications. Uses: Automotive exterior parts, profilesInformation provided by Basell.

Physical Properties	Metric	English	Comments
Density	1.03 g/cc	0.0372 lb/inÂ³	ASTM D792
Melt Flow	0.50 g/10 min @Load 2.16 kg, Temperature 230 Â°C	0.50 g/10 min @Load 4.76 lb, Temperature 446 Â°F	Condition L; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	68	68	ASTM D2240
Tensile Strength, Yield	23.0 MPa	3340 psi	ASTM D 638
Elongation at Break	450 %	450 %	ASTM D 638
Flexural Modulus	1.50 GPa	218 ksi	Tangent, 0.05 in/min; ASTM D790
	1.70 GPa	247 ksi	Tangent, 0.5 in/min; ASTM D790
Izod Impact, Notched	7.400 J/cm	13.86 ft-lb/in	73Â°F; ASTM D256
Gardner Impact	32.0 J @Temperature -30.0 Â°C	23.6 ft-lb @Temperature -22.0 Â°F	ASTM D3029
Tear Strength	140 kN/m	800 pli	ASTM D624

Thermal Properties	Metric	English	Comments
CTE, linear	47.0 Âµm/m-Â°C @Temperature -30.0 - 100 Â°C	26.1 Âµin/in-Â°F @Temperature -22.0 - 212 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	100 Â°C	212 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	57.8 Â°C	136 Â°F	Unannealed; ASTM D648