LyondellBasell Hifaxâ„¢ Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ CB252 medium high melt flow, 1,200 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has very well balanced processability, rigidity, impact resistance and paintability. It was designed primarily for automotive exterior ornamentation applications, but also has utility in certain interior trim components requiring high impact resistance. Uses: Automotive exterior and interior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ISO 1183 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | ISO 868 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527-1, -2 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-1, -2 |
| Elongation at Break | 450 % | 450 % | ISO 527-1, -2 |
| Elongation at Yield | 10 % | 10 % | ISO 527-1, -2 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.70 kJ/m² @Temperature -40.0 °C |
1.76 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 39.0 kJ/m² @Temperature 23.0 °C |
18.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop, Total Energy | 21.0 J @Temperature -30.0 °C |
15.5 ft-lb @Temperature -22.0 °F |
Instrumented Energy at Maximum Load, Ductile Failure; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 61.0 µm/m-°C @Temperature -30.0 - 100 °C |
33.9 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.2 °C | 180 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 °C | 117 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.70 % | 0.70 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 1.00 % @Temperature 121 °C, Time 3600 sec |
1.00 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Overview of materials for PVC, Foam Grade
- ITW Devcon Plastic Steel® Metal Repair 5 Minute® Putty (SF), Dark Grey
- Kuraray SEPTON® CM1 Compatibilizer
- SABIC Innovative Plastics NORYL SEH80 PPE+HIPS (Asia Pacific)
- Schott P-SK57 Glass
- Shinkong Synthetic Fibers Shinite® N601G30 Nylon 66, 30% Glass Filled
- CP-Polymer-Technik Wellamid® 6600/50 GV 15 HWCP 15% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Conditioned
- ExxonMobil LDPE LD 363BW Low Density Polyethylene Resin
- AlphaGary Evoprene™ 094 Standard SBS Thermoplastic Elastomer Compound
Copyright © lookpolymers.com All Rights Reserved