- LyondellBasell Higlass PF062-4 Polypropylene Homopolymer, 40% Glass Fiber
LyondellBasell Higlass PF062-4 Polypropylene Homopolymer, 40% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | LyondellBasell |
| Trade Name | Higlass |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Higlass PF062-4 Polypropylene Homopolymer, 40% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features: high melt flow, high modulus, chemically coupled, glass fiber-reinforced polypropylene homopolymer, high rigidity, high strength, excellent processabilityApplications: appliance parts, automotive components, electrical connectorsDescription: Higlass PF062-4 high melt flow, chemically coupled, 40% glass fiber-reinforced polypropylene homopolymer has an excellent combination of strength, rigidity and processability.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | Tool, Montell |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | Tangent at 0.05 in/min; ASTM D790A |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |