LyondellBasell Hostacomâ„¢ 62F4-2C Polypropylene Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer LyondellBasell
Trade Name Hostacom™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Hostacomâ„¢ 62F4-2C Polypropylene Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Hostacomâ„¢ 62F4-2C high melt flow, 1,900 MPa flexural modulus, precolored, 20% talc-filled polypropylene homopolymer has excellent heat aging characteristics, high chemical resistance and easy processability. Uses: Appliances, automotive applications, electrical parts, household goodsInformation provided by Basell.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
ASTM D955
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 230 °C
20 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Condition L; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 98
98
ASTM D 785
Tensile Strength at Break 26.0 MPa
3770 psi
ASTM D 638
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D 638
Elongation at Break 20 %
20 %
ASTM D 638
Elongation at Yield 5.0 %
5.0 %
ASTM D 638
Flexural Modulus 1.90 GPa
276 ksi
Tangent, 0.05 in/min; ASTM D790
Izod Impact, Notched 0.272 J/cm
0.510 ft-lb/in
73°F; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 116 °C
241 °F
Unannealed; ASTM D648