LyondellBasell Hostacomâ„¢ CB267 Thermoplastic Polyolefin Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin
Manufacturer LyondellBasell
Trade Name Hostacom™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Hostacomâ„¢ CB267 Thermoplastic Polyolefin Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Hostacomâ„¢ CB267 medium melt flow, 1,600 MPa flexural modulus thermoplastic elastomeric olefin (TEO) resin has an excellent balance of scratch and mar resistance, rigidity and impact resistance. It was designed primarily for molded-in color automotive instrument panel applications. Uses: Automotive interior partsInformation provided by Basell.
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
ISO 1183
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Condition L; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 95
95
ISO 2039-2
Hardness, Shore D 64
64
ISO 868
Tensile Strength, Yield 33.0 MPa
4790 psi
ISO 527-1, -2
Elongation at Break 100 %
100 %
ISO 527-1, -2
Flexural Modulus 1.60 GPa
232 ksi
ISO 178
Izod Impact, Notched (ISO) 4.50 kJ/m²

@Temperature -40.0 °C
2.14 ft-lb/in²

@Temperature -40.0 °F
ISO 180
15.0 kJ/m²

@Temperature 10.0 °C
7.14 ft-lb/in²

@Temperature 50.0 °F
ISO 180
40.0 kJ/m²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
CTE, linear 57.0 µm/m-°C

@Temperature -30.0 - 100 °C
31.7 µin/in-°F

@Temperature -22.0 - 212 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
Unannealed; ISO 75B-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 51.1 °C
124 °F
Unannealed; ISO 75A-1, -2
Shrinkage 1.3 %
1.3 %
Tool, 100x150x3.2 mm; Basell Test Method