LyondellBasell Lupolen® 4261 A HDPE, Blow Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | LyondellBasell |
| Trade Name | Lupolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Lupolen® 4261 A HDPE, Blow Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy-to-process bow molding grade for technical containers such as fuel tanks, petrol filler inlets, expansion tanks, horticultural spray tanks, tanks for lawnmowers, disposable containers (up to 1000 l), containers for transportation and storage, etc.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | |
| Water Absorption | 0.010 % | 0.010 % | |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | |
| High Load Melt Index | 0.10 g/10 min @Load 21.6 kg, Temperature 190 °C |
0.10 g/10 min @Load 47.6 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 10 % | 10 % | |
| Tensile Modulus | 0.850 GPa | 123 ksi | |
| Tensile Impact Strength | 260 kJ/m² | 124 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 360 MPa | 52200 psi | |
| Tensile Creep Modulus, 1000 hours | 250 MPa | 36300 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 170 µm/m-°C @Temperature 20.0 °C |
94.4 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 130 °C | 266 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | |
| Vicat Softening Point | 75.0 °C | 167 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
|
| Oxygen Index | 17 % | 17 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.4 @Frequency 100 Hz |
2.4 @Frequency 100 Hz |
|
| 2.4 @Frequency 1e+6 Hz |
2.4 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 150 kV/mm | 3810 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Iran Petrochemical (PCC) TG 641 Super Bright Polyethylene Terephthalate
- H.C. Starck Amperit® 515.2 Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12
- Lucite International Elvacite ® 2045 Acrylic Resin
- Solvay ALKAMIDE® DIN-295/S Surfactant
- Teknor Apex Sinpolene MBB1411 Linear Low Density Polyethylene
- A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT
- ArcelorMittal HSLA 460 High strength low alloy steel for cold forming, Hot Rolled
- EMS-Grivory Grivory® GV-4H black PA*-GF40
- CeramTec 975 Alumina, 99.5%
Copyright © lookpolymers.com All Rights Reserved